质量控制与失效分析 DOI:10.11973/lhjy-wl230332

滑轨钢边部细线缺陷产生原因

刘向明，王 伟，陈立平，李 欢，侯永亮
（首钢京唐钢铁联合有限责任公司，唐山 063200）

摘 要：针对某热镀锌产线出现的滑轨钢表面边部细线缺陷问题，采用宏观观察、扫描电镜及能
谱分析方法对缺陷产生原因进行分析。结果表明：细线缺陷由一层Ni、Co元素形成的异常层引起，
产生于热轧、精轧工序之前，由外部引入；缺陷产生原因为结晶器铜板镀层成分脱落进入铸坯。
关键词： 边部细线；缺陷；结晶器；铜板镀层；脱落
中图分类号：TB31；TG115.2 文献标志码：B 文章编号：1001-4012(2025)01-0037-04
Causes of thin line defects on the edge of slide rail steel

LIU Xiangming, WANG Wei, CHEN Liping, LI Huan, HOU Yongliang

(Shougang Jingtang United Iron & Steel Co.,Ltd., Tangshan 063200, China)
Abstract: Aiming at the problem of thin line defect on the surface edge of slide rail steel in a hot-dip galvanizing
production line, the causes of the defects were analyzed by macroscopic observation, scanning electron microscope and
energy spectrum analysis. The results show that the thin wire defect was caused by an abnormal layer formed by a layer of Ni
and Co elements, which was produced before the hot rolling and finishing rolling processes and introduced from the outside.

The cause of the defect was that the coating composition of the crystallizer copper plate fell off into the slab.
Keywords: edge thin line; defect; crystallizer; copper plate coating; falling off

边部细线缺陷在炼钢、连铸、热轧、冷轧、连退、
涂镀等工序均可产生。炼钢工序中的夹杂物，连铸
工序连铸坯边角部的受力状态、传热状态 [1-3] ，以及
热轧、冷轧过程划伤均可导致边部细线 [4-6] 。边部细
线缺陷影响产品质量，可批量出现，严重时会造成巨
[7]
大的经济损失 。某产线生产镀锌产品滑轨钢时，
产品边部出现通卷断续分布的细线缺陷，严重影响
了生产节奏及产品质量。笔者采用一系列理化检验
图 1 边部细线缺陷试样宏观形貌
方法分析了细线缺陷的产生原因，以防止该类问题
在细线缺陷。
再次发生。
1.2 扫描电镜 （SEM）和能谱分析
1 理化检验 将盐酸与水同比例混合后加入缓蚀剂，配置成
1.1 宏观观察 脱锌层酸洗液。通过酸洗去除锌层后，在基板缺陷

镀锌成品卷的边部细线缺陷试样宏观形貌如 位置截取试样，将试样置于扫描电子显微镜下观察，
图1所示。缺陷位于带钢上表面操作侧，宽度方向 结果如图2所示。由图2可知：基板细线缺陷位置存
基本固定，经过切边后，与宽度方向边部的距离约为 在一层异常层，部分区域异常层与基板脱离，形成起
10 mm。距离热轧卷宽度方向边部约20 mm同样存 皮形貌。

对基板缺陷处进行能谱分析，结果如图3所示。
收稿日期：2023-11-27
由图3可知： 异常层的成分主要为Ni、Co、Al等元素。
作者简介：刘向明（1992—），男，硕士，工程师，主要从事金属
材料分析方面工作，1249932260@qq.com 从成分元素的构成及含量来看，异常层明显不同于
37