ANALYSIS OF ONE KIND OF SADP OF Fe2Al5 PHASE

ZHANG Jin-min. ANALYSIS OF ONE KIND OF SADP OF Fe2Al5 PHASE[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2007, 43(8): 407-408.

Citation:

ZHANG Jin-min. ANALYSIS OF ONE KIND OF SADP OF Fe2Al5 PHASE[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2007, 43(8): 407-408.

Citation:

ZHANG Jin-min. ANALYSIS OF ONE KIND OF SADP OF Fe2Al5 PHASE[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2007, 43(8): 407-408.

Abstract

The Fe2Al5 phase of coating hot-dipped with aluminum was analyzed by transmission electron microscopy (TEM). The results show that one kind of select area electron diffraction pattern (SADP) of Fe2Al5 phase is similar with hexagon. However,its SADP is not hexagon by analyzing. So it is considered that belongs to orthorhombic crystalline system.