KEEPING AWAY FROM ERODED ON SUS301 STAINLESS STEEL DURING PRODUCTION

During the cool rolling process of SUS301 stainless steel,the punctual flaws and cracks are offen observed. Intergranular corrosion cause the flaws. Increasing the temperature annealing during the cool rolling can avoid the flaws parcel on some extent. Buts electing the suitable whirling temperature is the primary method to prevent above defects.