ZHANG Kun, CHEN Guang-nan, PENG Yu-chun. ON THE ORIGIN OF SUBSTRATE EROSION IN CHROMIUM PLATED GUN BARREL[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2006, 42(4): 171-173.
Citation:
ZHANG Kun, CHEN Guang-nan, PENG Yu-chun. ON THE ORIGIN OF SUBSTRATE EROSION IN CHROMIUM PLATED GUN BARREL[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2006, 42(4): 171-173.
ZHANG Kun, CHEN Guang-nan, PENG Yu-chun. ON THE ORIGIN OF SUBSTRATE EROSION IN CHROMIUM PLATED GUN BARREL[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2006, 42(4): 171-173.
Citation:
ZHANG Kun, CHEN Guang-nan, PENG Yu-chun. ON THE ORIGIN OF SUBSTRATE EROSION IN CHROMIUM PLATED GUN BARREL[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2006, 42(4): 171-173.
ON THE ORIGIN OF SUBSTRATE EROSION IN CHROMIUM PLATED GUN BARREL
In order to reveal the relation between the fabrication process and erosion life of chromium plated gun barrel used in model products, the eroded gun barrel with four different fabrication processes have been examined. It has been found that three different erosion modes, i.e. interface erosion, sub-interface erosion and penetrating erosion correspond to the low, medium and high erosion life, respectively.