DONG Jia-Kun. A SORT OF SENSITIVE ERODING REAGENT ON SPOT ERODING OF MARTENSITE STAINLESS STEEL[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2008, 44(2): 82-83.
Citation: DONG Jia-Kun. A SORT OF SENSITIVE ERODING REAGENT ON SPOT ERODING OF MARTENSITE STAINLESS STEEL[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2008, 44(2): 82-83.

A SORT OF SENSITIVE ERODING REAGENT ON SPOT ERODING OF MARTENSITE STAINLESS STEEL

More Information
  • Received Date: September 21, 2006
  • Spot eroding is easily observed when martensite stainless steel is eroded by solution of HF,HNO3 and H2O,with macula shape. Hence the sort of eroding reagent can be applied to inspection of spot eroding tendency on martensite stainless steel. Operation and statistic for years shows that spot eroding resistance of refining steel is obviously better than that of conventional steel,so the sort of eroding reagent can be applied to assessing of quality of martensite stainless steel.
  • [1]
    陈德和.不锈钢及其热处理[M].北京:机械工业出版社,1973.
    [2]
    董加坤.一种显示马氏体不锈钢组织的金相侵蚀剂[J].理化检验-物理分册,2006,42(1):48-49.
  • Related Articles

    [1]XU Liju, LEI Zhiliang, GAO Xingjian, ZHAO Zhenwei. Effect of different refining modes on the quality of weathering steel Q355GNH[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2024, 60(8): 1-5. DOI: 10.11973/lhjy-wl240049
    [2]YIN Yahao, GUO Lei, CHEN Xiaodong, SU Jianfeng, LIU Yang. Fracture reasons of prestressed finish rolled screw-thread steel bars[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2023, 59(9): 23-26. DOI: 10.11973/lhjy-wl202309007
    [3]LI Hongyuan, ZHANG Yanzhao, ZHANG Zhouyong, LIU Hongqun, PAN Yaofan. Causes of leakage of austenitic stainless steel instrumentation pipe for essential service water system in a nuclear power plant[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2022, 58(3): 45-48. DOI: 10.11973/lhjy-wl202203013
    [4]HU Zhan, WU Changbai. Structure and Properties of B Grade Ship Plates Produce by Different Refining Processes[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2018, 54(11): 794-798,818. DOI: 10.11973/lhjy-wl201811003
    [5]FAN Zhi-jin, LUO Guo-hua, XU Zhi-dong, WANG Rui-min. Cleanliness of GCr15 Bearing Steel Produced by Hot Metal Pretreatment→120 t LD→LF→RH→CC Process[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2011, 47(12): 744-747.
    [6]PAN Hong-tao. Metallograhic Examination of Inclusion in Q235B Liquid Steel before and after Refining[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2009, 45(8): 495-496.
    [7]WEN Jia-hui, HU Chuan-shun, XIAO Kai, WANG Jie. Corrosive Pitting Behavior of 316L Stainless Steel Welding Seam[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2009, 45(4): 205-207.
    [8]ZHANG Bo, HU Qing-song, JIN Long. KEEPING AWAY FROM ERODED ON SUS301 STAINLESS STEEL DURING PRODUCTION[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2008, 44(2): 61-63.
    [9]CHEN Xia, LI Chen-hui. EFFECT OF PRECURSORS PHASE COMPOSITION ON ITO WITH THE RIETVELD REFINMENT[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2007, 43(11): 548-551.
    [10]DONG Jia-kun. A METALLOGRAPHIC CORRADING AGENT SHOWING MARTENSITIC STAINLESS STEEL STRUCTURE[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2006, 42(1): 48-49.

Catalog

    Article views (3) PDF downloads (1) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return