WANG Siqin, GAO Xingjian, LEI Zhiliang. Effect of hot rolling heating time on electromagnetic properties and inclusions of 1.8%Si non-oriented silicon steel[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2024, 60(10): 42-46. DOI: 10.11973/lhjy-wl240153
Citation: WANG Siqin, GAO Xingjian, LEI Zhiliang. Effect of hot rolling heating time on electromagnetic properties and inclusions of 1.8%Si non-oriented silicon steel[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2024, 60(10): 42-46. DOI: 10.11973/lhjy-wl240153

Effect of hot rolling heating time on electromagnetic properties and inclusions of 1.8%Si non-oriented silicon steel

More Information
  • The electromagnetic properties of 1.8%Si non-oriented silicon steel with different heating time were compared, the change rules of microstructure and inclusions were analyzed. The results show that the iron loss of the sample with long heating time in the hot rolling furnace was 0.43 W/kg, which was mainly because there were a large number of AlN inclusions with size less than 1 μm and irregular shape pinned at the grain boundary, which led to the failure of grain growth and the fine and uneven grain structure. A large amount of AlN was uniformly dissolved in the slab by heating furnace at 1 000~1 120 ℃ for a long time. In the process of rolling and cooling, AlN was precipitated in a dispersed and fine state and inherited into the cold coil. In the continuous heat treatment process of silicon steel unit, when the temperature reached above 950 ℃, AlN was precipitated in a dispersed and fine form after solid solution again. For the samples with normal heating time, even in the case of high temperature in the soaking section of the heating furnace, because AlN was not uniformly dissolved in each position of the slab, AlN was precipitated in a clustered state during rolling and cooling. The inclusions were mainly AlN, CaS-Al2O3, AlN-CaO-Al2O3 composite inclusions with relatively large size, and the electromagnetic properties were good.

  • [1]
    万勇,陈伟庆,吴绍杰 .铸坯热装温度对无取向硅钢中AlN和MnS析出行为的影响[J].北京科技大学学报,2013,20(8):1007-1014.
    [2]
    王茹玉 .热轧加热温度对3.0%Si无取向硅钢组织及析出物的影响[J].电工钢,2020,2(2):11-15.
    [3]
    罗小燕,朱诚意,李光强,等 .热装温度对无取向硅钢中夹杂物析出特性的影响[J].武汉科技大学学报(自然科学版),2018,41(1):8-14.
    [4]
    姜世勇,李俊虎,张文康 .热轧工艺对无取向硅钢组织结构的影响[J].电工材料,2006(2):13-16.
    [5]
    赵有明,游光明,冷烨旻,等 .50W600冷轧无取向电工钢铁损偏高原因分析[J].江西冶金,2013,33(3):25-28.
    [6]
    JIAO H T ,XU Y B ,XU H J ,et al .Influence of hot deformation on texture and magnetic properties of strip cast non-oriented electrical steel[J].Journal of Magnetism and Magnetic Materials,2018,462:205-215.
    [7]
    WANG J ,LI J ,WANG X F ,et al .Effect of heating rate on microstructure evolution and magnetic properties of cold rolled non-oriented electrical steel[J].Journal of Iron and (下转第51页)Steel Research,International,2010,17(11):54-61.
    [8]
    LIU H T ,LIU Z Y ,CAO G M ,et al .Microstructure and texture evolution of strip casting 3wt% Si non-oriented silicon steel with columnar structure[J].Journal of Magnetism and Magnetic Materials,2011,323(21):2648-2651.
    [9]
    LAN M F ,ZHANG Y X ,FANG F ,et al .Effect of annealing after strip casting on microstructure,precipitates and texture in non-oriented silicon steel produced by twin-roll strip casting[J].Materials Characterization,2018,142:531-539.
    [10]
    乔家龙,郭飞虎,胡金文,等 .无取向硅钢中氮化物的析出机理[J].材料热处理学报,2021,42(1):110-118.
    [11]
    张文康,毛卫民,王一德,等 .热轧工艺对无取向硅钢组织结构和磁性能的影响[J].钢铁,2006,41(4):77-81.

Catalog

    Article views (14) PDF downloads (0) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return