    PENG Shuang, SUN Zhijun, JIN Yi, TENG Yuefei, CAO Wei. The reason for the difference in fatigue performance of TC17 titanium alloy circular perforated plate specimens[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2023, 59(4): 31-37. DOI: 10.11973/lhjy-wl202304009
    Citation: PENG Shuang, SUN Zhijun, JIN Yi, TENG Yuefei, CAO Wei. The reason for the difference in fatigue performance of TC17 titanium alloy circular perforated plate specimens[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2023, 59(4): 31-37. DOI: 10.11973/lhjy-wl202304009

    The reason for the difference in fatigue performance of TC17 titanium alloy circular perforated plate specimens

    • The fatigue properties of TC17 titanium alloy circular perforated plate specimens were different. The reason for the differences was analyzed by scanning electron microscopy and energy spectrum analysis, metallographic examination, residual stress test and roughness test. The results show that for the plate-shaped circular hole fatigue specimen with Kt=2.52 and short life, the fatigue crack originated from the processing damage at the rounding of the hole edge or the processing damage of the inner wall of the hole, and the fatigue cracks of the longer life specimen originated from the inner wall of the hole. For the plate-shaped hole fatigue specimen with Kt=2.1 and short life, the fatigue crack originated from the machining damage of the inner wall of the hole or the rounding damage of the hole edge, while the fatigue cracks of the long-life specimen mostly originated from the surface machining defects or the subsurface of the inner wall of the hole. The fatigue properties of the samples were greatly different due to the processing damage of the samples, the large residual compressive stress on the inner wall of the hole and the dispersion of the residual stress.
    • loading

    Catalog

      Turn off MathJax
      Article Contents

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return