ZHENG Qiu-yan, ZHAO Jian-ming. A Kind of Slow Aerated Method for H2S Corrosin Resistance Performance Test[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2015, 51(8): 575-577. DOI: 10.11973/lhjy-wl201508011
Citation: ZHENG Qiu-yan, ZHAO Jian-ming. A Kind of Slow Aerated Method for H2S Corrosin Resistance Performance Test[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2015, 51(8): 575-577. DOI: 10.11973/lhjy-wl201508011

A Kind of Slow Aerated Method for H2S Corrosin Resistance Performance Test

More Information
  • Received Date: June 04, 2015
  • A kind of slow aerated method was proposed when carrying out sulfide stress corrosion (SSC-A)test and hydrogen induced cracking (HIC)test according to the standard of NACE TM0177-2005 and NACE TM0284-2011 respectively,and iodometric method was used to measure the mass concentration of H2S in the solution.At the same time,the time of H2S reaching saturation and the pH value of the solution were studied.The results show that every SSC-A test and HIC test could save 800 mL and 1 695 mL H2S gas respectively after adopting slow aerated method compared to original fast aerated method required in NACE TM0177-2005 and NACE TM0284-2011.So slow aerated method can greatly reduce the test cost and emissions of toxic gas H2S,as well as ensure the reliability and authenticity of the test results.
  • [1]
    尹成先.X70管线钢氢致开裂及应力腐蚀腐蚀行为研究[D].西安:西安建筑科技大学,2003.
    [2]
    周丽萍,穆海玲,赵楠.X52管线钢抗氢致开裂试验裂纹成因分析[J].理化检验-物理分册,2013,49(4):270-275.
    [3]
    李家鼎,李少坡,查春和,等.抗酸钢中产生氢致裂纹与氢鼓包的原因分析[J].理化检验-物理分册,2013,49(1):22-27.
    [4]
    刘智勇,李明,李晓刚.油田硫化氢腐蚀机理及防护的研究现状及进展[J].中国腐蚀与防护学报,2006,26(4):83-86.
    [5]
    NACE TM0177-2005Laboratory testing of metals for resistance to sulfide stress cracking and stress corrosion cracking in H2S environments[S].
    [6]
    NACE TM0284-2011Evaluation of pipeline and pressure vessel steels for resistance to hydrogen-induced cracking[S].

Catalog

    Article views (2) PDF downloads (1) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return